Savoy Piping Inc., we carry a full inventory of ASTM A213 TP309s Stainless Steel Seamless Pipe and Supply ASTM A213 TP309s Stainless Steel Seamless Pipe austenitic chromium-nickel stainless steel pipe suitable for corrosive or high-temperature service, or both, or for general applications.
We Supply ASTM A213 TP309s Stainless Steel Seamless Pipes in Grades in Specification ASME SA / ASTM A269, A312, A213 and along with other Grades 202, 304, 304L, 304H, 304LN, 309s, 310s, 316, 316L, 316H, 316Ti, 316LN, 317L, 321, 321H, 347, 347H, 904L, 254 SMO, 6MO, 6 MOLY, UNS S31254, etc. The grade indicates the testing methods required for a given application.
Savoy Piping Inc. specializes in ASTM A213 TP309s Stainless Steel Seamless Pipe with years of Experience in Manufacturing ASTM A213 TP309s Stainless Steel Seamless Pipe. we offer high quality, lower cost but the best service. As a result to that our ASTM A213 TP309s Stainless Steel Seamless Pipes export account today is in various countries like Iran, Iraq, Kuwait, Saudi Arabia, Oman, UAE, Singapore, Malaysia, Indonesia, South korea, Chile, Peru, Venezuela, Australia, Nigeria, Angola, Senegal, Mozambique, Algeria, Libya, Azerbaijan, Netherlands, Brazil, Norway, United Kingdom, Mexico, Canada etc.
ASTM A213 TP309s Stainless Steel Seamless Pipes Manufacturer, Stockholder and Supplier
Stainless Steel is often Referred to as Corrosion-Resistant Steel – it does not stain, Corrode or Rust as easily as Normal Carbon Steel. It would however be misleading to say it is Corrosion-Proof. It differs significantly from standard Carbon Steel due to the amount of Chromium present, which limits surface Corrosion unlike Carbon Steel which will Rust when exposed to air and any moisture in the Atmosphere. Due to its Anti-Oxidation Qualities, Stainless Steel is often a Popular Solution.
Where low maintenance and corrosion resistance is required, stainless steel plates are a natural choice and are used in a diverse range of applications from modern Architecture for cladding or fascia’s, to the food hygiene industry due to its Anti-Bacterial Qualities. Savoy Piping Inc., Supplies Stainless Steel in a wide variety of Grades and Aesthetic Finishes. There are many options available - for example adding carbon during the forming process will make the stainless steel more durable and stronger too.
Stainless Steel Seamless (SMLS) pipe is formed by drawing a solid billet over a piercing rod to create the hollow shell. As the manufacturing process does not include any welding, Seamless Pipes are perceived to be stronger and more reliable. Historically, seamless pipe was regarded as withstanding pressure better than other types, and was often more available than Welded Pipe.
Alloys 309 and Alloys 309S are austenitic chromium-nickel stainless steels that are often used for higher temperature applications. Due to their high chromium and nickel content, Alloys 309 and 309S are highly corrosion resistant, have outstanding resistance to oxidation, and excellent heat resistance while providing good strength at room and elevated temperatures. The only significant difference between 309 and 309S is the carbon content. Alloy 309S has a much less carbon composition which minimizes carbide precipitation and improves weldability.
Alloy 309 (UNS S30900) is an austenitic stainless steel developed for use in high temperature corrosion resistance applications. The alloy resists oxidation up to 1900°F (1038°C) under non-cyclic conditions. Frequent thermal cycling reduces oxidation resistance to approximately 1850°F (1010°C).
Because of its high chromium and low nickel content, Alloy 309 can be utilized in sulfur containing atmospheres up to 1832°F (1000°C). The alloy is not recommended for use in highly carburizing atmospheres since it exhibits only moderate resistance to carbon absorption. Alloy 309 can be utilized in slightly oxidizing, nitriding, cementing and thermal cycling applications, albeit, the maximum service temperature must be reduced.
When heated between 1202 – 1742°F (650 – 950°C) the alloy is subject to sigma phase precipitation. A solution annealing treatment at 2012 – 2102°F (1100 – 1150°C) will restore a degree of toughness.
309S (UNS S30908) is the low carbon version of the alloy. It is utilized for ease of fabrication. 309H (UNS S30909) is a high carbon modification developed for enhanced creep resistance. It most instances the grain size and carbon content of the plate can meet both the 309S and 309H requirements.
Alloy 309 can be easily welded and processed by standard shop fabrication practices.
Specifications: UNS S30900 / S30908
|ASTM A213 TP309s Stainless Steel Seamless Pipes Specification||ASTM A269, ASTM A213, ASTM A213, ASME SA269, ASME SA213, ASME SA213|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Grades||202, 304, 304L, 304H, 304LN, 309S, 310S, 316, 316L, 316H, 316Ti, 316LN, 317L, 321, 321H, 347, 347H, 904L, SMO 254, ALLOY 254, 6MO, 6MOLY, UNS S31254 ETC.|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Type||Seamless / Welded / ERW / EFW / Cold Draw / Hot Finish / Cold Finish|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Outer Diameter Size|| Seamless - 1/2" NB TO 18" NB
Welded / ERW- 1" NB TO 16" NB
EFW - 8" NB TO 110" NB
|ASTM A213 TP309s Stainless Steel Seamless Pipes Wall Thickness||Schedule 10 to Schedule 160 (3 mm to 100 mm Thickness)|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Length||01 Meter to 12.5 Meters, Single Random Length, Double Random Length And Customize Size.|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Ends||Plain Ends / Beveled Ends|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Delivery Conditions||As Rolled, Formed, Stress Relieved, Annealed, Hardened, Tempered, Cold Draw|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Coating||Electropolish, Mechanical Polish, Satin Finish, Passivated|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Other Testing||Product Analysis, Transverse Tension Test, Flattening Test, Etching Test, Radiograph HIC Examination, Stabilizing Heat Treatment, Intergranular Corrosion Test, Weld Decay Test, Magnetic Particle Detection, Grain Size Test, NACE 0175, Dual Grade, PWHT (POST WELD HEAT TREATMENT), Flare Test, Bend Test, Hardness Test, Tensile Test etc|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Dimension||All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Value Added Services||Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment / Annealed / Bright Annealed|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Packaging||Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Shipment & Transportation||By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes|
|ASTM A213 TP309s Stainless Steel Seamless Pipes Material Test Certificate||Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC
The chemical composition of grade 309S Stainless Steel is outlined in the following table
|Chromium||22.0 min.-24.0 max.||22.0 min.-24.0 max.||22.0 min.-24.0 max.|
|Nickel||12.0 min.-15.0 max.||12.0 min.-15.0 max.||12.0 min.-15.0 max.|
|Carbon||0.20||0.08||0.04 min.-0.10 max.|
The Mechanical Properties of grade 309S Stainless Steel are displayed in the following table.
|Tensile strength, ultimate||620 MPa||89900 psi|
|Tensile strength, yield (0.2%)||310 MPa||45000 psi|
|Izod impact||120 - 165 J||88.5 - 122 ft-lb|
|Modulus of elasticity||200 GPa||29000 ksi|
|Shear modulus||77 GPa||11200 ksi|
|Elongation at break (in 50 mm)||45%||45%|
|Hardness, Brinell (converted from Rockwell B hardness)||147||147|
|Hardness, Knoop (converted from Rockwell B hardness)||164||164|
|Hardness, Rockwell B||85||85|
|Hardness, Vickers (converted from Rockwell B hardness)||169||169|
Physical properties of 309s grade stainless steel in the annealed condition
|Density||8 g/cm3||0.289 lb/in³|
Grade specifications for 309s grade stainless steel
|Thermal expansion co-efficient (@ 0-100°C/32-212°F)||14.9 µm/m°C||8.28 µin/in°F|
|Thermal conductivity (@0-100°C/32-212°F)||15.6 W/mK||108 BTU in/hr.ft².°F|
The grade 309S steel can be made into plates, sheets, and coils to be used in the following:
We Export ASTM A213 TP309s Stainless Steel Seamless Pipes to Saudi Arabia, Iran, Iraq, United Arab Emirates, Qatar, Bahrain, Oman, Kuwait, Turkey, Egypt, Yemen, Syria, Israel, Jordan, Cyprus, Singapore, Malaysia, Indonesia, Thailand, Vietnam, South Korea, Japan, Sri Lanka, Maldives, Bangladesh, Mayanmar, Taiwan, Cambodia, Argentina, Bolivia, Brazil, Chile, Venezuela, Colombia, Ecuador, Guyana, Paraguay, Uruguay, United States of America, Canada, Mexico, Panama, Costa Rica, Puerto Rica, Trinidad And Tobago, Jamaica, Bahamas, Denmark, Russia, Norway, Germany, France, Italy, United Kingdom, Spain, Ukraine, Netherland, Belgium, Greece, Czech Republic, Portugal, Hungary, Albania, Austria, Switzerland, Slovakia, Finland, Ireland, Croatia, Slovenia, Malta, Nigeria, Algeria, Angola, South Africa, Libya, Egypt, Sudan, Equatorial Guinea, The Republic Of Congo, Gabon, Europe, Africa, Asia, North America, South America, Middle East, Far East.etc
Savoy Piping Inc. is a well known worldwide Exporter of ASTM A213 TP309s Stainless Steel Seamless Pipes, Savoy Piping Inc. is committed to provide each and every customer with the highest standard of customer service. We deals in ASTM A213 TP309s Stainless Steel Seamless Pipe in India and Overseas, offering a wide range of ASTM A213 TP309s Stainless Steel Seamless Pipes .